HUATECH 橡胶修复材料是一种全新的单组份橡胶颗粒材料,通过直接热熔的方法进行操作,极大的降低了操作难度,克服了传统双组份修复材料对环境和操作人员的高要求。特殊高分子结构在保证具备良好热加工性的同时,还具备高耐磨性、韧性、阻燃性能。材料为100%无溶剂固体,不含任何挥发组分,在操作温度范围内无有毒物质析出或挥发。可在30分钟内完成固化,在输送带出现损伤时,及时进行冷修补,能够实现阻止输送带的损伤部位继续发生扩展、延伸,从而有效保护输送带的芯体免于受损。
1.检查防护工具和操作工具是否完全
2对待修复橡胶面进行清理、打磨
3 用酒精或者二甲苯对处理后的表面进行清洗,并用热风机吹干
4 取适量颗粒材料放在待修复部位,用热风枪进行加热,加热的时候注意保持热风与颗粒的距离(根据距离、温度而定,一般10-15cm),若修复部位损伤较深,需分多次进行修复,尽量保持每次修复时为单层颗粒平铺。
5 待修复厚度基本完成,再用热风枪加热修复表面和金属刮板(或是油灰刀),把修复的表面刮平。
6 冷却30分钟即可投入使用
HUATECH rubber repair material is a new one-component rubber particle material, which is operated by direct hot melt method, which greatly reduces the operation difficulty and overcomes the high requirements of the environment and operators of traditional two-component repair materials. The special polymer structure guarantees good hot workability and high wear resistance, toughness and flame retardancy. The material is 100% solvent-free solid, does not contain any volatile components, and no toxic substances are precipitated or volatilized within the operating temperature range. The curing can be completed within 30 minutes. When the conveyor belt is damaged, the cold repair can be carried out in time to prevent the damaged portion of the conveyor belt from continuing to expand and extend, thereby effectively protecting the core of the conveyor belt from damage.
1. Check if the protective tools and operating tools are completely
2 Clean and polish the rubber surface to be repaired
3 Wash the treated surface with alcohol or xylene and blow dry with a hot air blower
4 Take appropriate amount of granular material and place it on the part to be repaired. Heat it with a hot air gun. When heating, pay attention to keep the distance between hot air and particles (depending on distance and temperature, generally 10-15cm). If the damage of the repaired part is deep, it needs to be divided. Repair multiple times, try to keep the single layer of particles tiled each time you repair.
5 The thickness to be repaired is basically completed, and then the surface and the metal scraper (or putty knife) are heated by a heat gun to flatten the repaired surface.
6 Cool down for 30 minutes and put it into use